Electrical devices containing carbon nanotube-infused fibers and methods for production thereof

ABSTRACT

Electrical devices containing continuous fibers that are infused with carbon nanotubes are described herein. The electrical devices contain at least a first electrode layer and a second electrode layer, where the first and second electrode layers each contain a plurality of continuous fibers that are infused with carbon nanotubes. In some embodiments, the electrical devices can be supercapacitors, further containing at least a base plate, a layer of separator material disposed between the first and second electrode layers, and an electrolyte in contact with the first and second electrode layers. The first and second electrode layers can be formed by conformal winding of the continuous fibers. The electrical devices can contain any number of additional electrode layers, each being separated from one another by a layer of separator material. Methods for producing the electrical devices are also described herein.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of priority under 35 U.S.C. §119 from U.S. Provisional Patent Application Ser. No. 61/309,827, filed Mar. 2, 2010, which is incorporated herein by reference in its entirety.

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT

Not applicable.

FIELD OF THE INVENTION

The present invention generally relates to energy storage, and, more specifically, energy storage using carbon nanotubes.

BACKGROUND

Capacitors are electrical devices that are used to accumulate and store electric charge. Capacitors are distinguished from batteries in at least two aspects. First, storage of electric charge in a capacitor is based upon physical charge separation rather than the chemical separation of a battery. Second, charge and discharge rates of a capacitor are much more rapid than the chemical reactions that occur in a battery.

In conventional capacitors, charge separation is maintained by two conductive plates that are separated by a dielectric material. In the presence of an applied potential, an electric field builds in the dielectric material and produces a mechanical force between the conductive plates. The ratio of the electric charge maintained on the conductive plates to the potential difference between them is referred to as the capacitance, which is measured in Farads.

Various modifications of conventional capacitors have also been developed. Electrolytic capacitors utilize an ion-containing liquid as one of its conductive plates. Such electrolytic capacitors typically display much higher capacitance values than do conventional capacitors. However, their utility is somewhat limited by a requirement that each conductive plate is to be maintained in a polarized voltage state.

Supercapacitors, also known as electric double-layer capacitors, electrochemical double-layer capacitors, supercondensors, ultracapacitors, or pseudocapacitors, can display even higher capacitance values. Supercapacitors differ significantly from conventional capacitors and electrolytic capacitors in that there is not a significant physical separation of the conductive plates in a supercapacitor. Instead, supercapacitors maintain charge separation by incorporating a vanishingly thin physical barrier between the conductive plates (<100 μm). The physical barrier effectively maintains charge separation when the supercapacitor is in the charged state, while being sufficiently permeable to charge carriers to allow rapid charge and discharge rates.

Many conventional supercapacitors presently use activated carbon particles as a high surface area substrate to hold charge carriers from an electrolyte dispersed therein. Although activated carbon particles have a high surface area, certain charge carriers are too large to penetrate the porous interior of the activated carbon particles and take advantage of its high surface area. FIG. 1 shows a schematic of an illustrative prior art supercapacitor 100 containing activated carbon particles 105. Supercapacitor 100 contains conductive layers 101 and 102, connected to positive terminal 103 and negative terminal 104, respectively. Conductive layers 101 and 102 each contain activated carbon particles 105 and an electrolyte containing positive ions 106 and negative ions 107 admixed with activated carbon particles 105. Positive ions 106 and negative ions 107 can reside about the interior or exterior of activated carbon particles 105. Conductive layers 101 and 102 are physically isolated from one another by a layer of separator material 108, which is permeable to positive ions 106 and negative ions 107 of the electrolyte. As shown in FIG. 1, supercapacitor 100 is in a discharged state.

Certain high performance materials, including carbon nanotubes, have been proposed as a replacement for activated carbon particles in supercapacitors due their high accessible surface area. Carbon nanotubes can be further advantageous in this regard due to their electrical conductivity. Although carbon nanotubes have significant potential for improving the performance of supercapacitors, research efforts to date have only been successful in randomly dispersing small quantities of carbon nanotubes in the electrolyte medium of a supercapacitor. As such, current fabrication techniques are only amenable to production of small carbon nanotube-containing supercapacitors with low electrical storage capabilities.

In view of the foregoing, high-volume supercapacitors and other electrical devices containing large quantities of carbon nanotubes would be of significant benefit in the art. It would also be of considerable benefit to provide methods for readily preparing such high-volume supercapacitors having enhanced electrical storage capabilities. The present invention satisfies these needs and provides related advantages as well.

SUMMARY

In some embodiments, electrical devices described herein include a first electrode layer and a second electrode layer, where the first electrode layer and the second electrode layer contain a plurality of continuous fibers that are infused with carbon nanotubes.

In some embodiments, methods described herein include providing a plurality of continuous fibers that are infused with carbon nanotubes, forming a first electrode layer from a first portion of the plurality of continuous fibers, and forming a second electrode layer from a second portion of the plurality of continuous fibers.

In other embodiments, methods described herein include providing a plurality of continuous fibers that are infused with carbon nanotubes, forming a first electrode layer by winding a portion of the plurality of continuous fibers conformally about a base plate, and forming at least two additional electrode layers over the first electrode layer by winding separate portions of the plurality of continuous fibers conformally over the first electrode layer.

The foregoing has outlined rather broadly the features of the present disclosure in order that the detailed description that follows can be better understood. Additional features and advantages of the disclosure will be described hereinafter, which form the subject of the claims.

BRIEF DESCRIPTION OF THE DRAWINGS

For a more complete understanding of the present disclosure, and the advantages thereof, reference is now made to the following descriptions to be taken in conjunction with the accompanying drawings describing a specific embodiments of the disclosure, wherein:

FIG. 1 shows a schematic of an illustrative prior art supercapacitor containing activated carbon particles;

FIG. 2A shows an isometric schematic of the first electrode layer in an illustrative embodiment of the present supercapacitors; FIG. 2B shows an isometric schematic of the first electrode layer in an illustrative embodiment of the present supercapacitors in which an electrode terminal is located on the base plate;

FIG. 3 shows a schematic of an illustrative embodiment of the present supercapacitors as viewed parallel to the longitudinal axes of the continuous fibers of the electrode layers;

FIG. 4 shows a schematic of a coin press sample supercapacitor structure; and

FIG. 5 shows an illustrative cyclic voltammogram of a supercapacitor of the present disclosure.

DETAILED DESCRIPTION

The present disclosure is directed, in part, to electrical devices containing electrode layers formed from continuous fibers that have been infused with carbon nanotubes. Such continuous fibers are also referred to herein as carbon nanotube-infused fibers or carbon nanotube-infused fiber materials. The present disclosure is also directed, in part, to methods for making electrical devices having electrode layers formed from continuous fibers that have been infused with carbon nanotubes.

As previously set forth, supercapacitors typically display much higher capacitance values than do conventional capacitors or electrolytic capacitors. Accordingly, they have garnered significant interest in energy storage applications such as solar energy collection, hydroelectric energy collection, and wind farm energy collection. The rapid charge and discharge cycles of supercapacitors make them well suited for these purposes and others, since the supercapacitors can readily take on excess energy when electrical grid demand is low and quickly release their stored energy when electrical grid demand is high. Further, supercapacitors are capable of being non-degradably charged and discharged many hundreds of thousands of times, making them considerably superior to batteries in this regard. In addition, the rapid charge and discharge cycles of supercapacitors and their charge/discharge stability make them particularly useful for applications in which multiple cycles of rapid charging and discharging are desirable such as, for example, in hybrid gas-electric vehicles.

With growing interest in the above applications and others, supercapacitors that have even higher energy storage limits than those currently available are needed. The capacitance in supercapacitors is proportional to the electrode surface area (e.g., the area of the conductive plates). In conventional supercapacitors containing activated carbon particles, there is an intrinsic limit as to how much the effective electrode surface area can be increased. That is, the activated carbon particles used in conventional supercapacitors can only be made so small before an asymptotic capacitance value is reached. Further, limited pore sizes in the activated carbon particles reduce their effective surface area and can be problematic for some electrolytes. Because carbon nanotubes provide a much higher effective surface area per unit weight than does activated carbon, these entities offer the potential to significantly increase the capacitance of supercapacitors. Despite their promise in supercapacitor applications, it has heretofore been difficult to place carbon nanotubes into supercapacitors in a state that can take advantage of their exceedingly high effective surface area.

Embodiments of the present disclosure describe electrical devices containing electrodes made from continuous fibers that have been infused with carbon nanotubes. Such continuous carbon nanotube-infused fibers are described in commonly assigned, co-pending U.S. patent application Ser. Nos. 12/611,073, 12/611,101, and 12/611,103, all filed on Nov. 2, 2009, and Ser. No. 12/938,328, filed on Nov. 2, 2010, each of which is incorporated herein by reference in its entirety. The fiber material of such carbon nanotube-infused fibers can generally vary without limitation and can include, for example, glass fibers, carbon fibers, metal fibers, ceramic fibers, and organic fibers (e.g., aramid fibers) for example. Such carbon nanotube-infused fibers can be readily prepared in spoolable lengths from commercially available continuous fibers or continuous fiber forms (e.g., fiber tows or fiber tapes). In addition, the carbon nanotubes' lengths, diameter, and coverage density can readily be varied by the above-referenced methods.

Depending on their growth conditions, the carbon nanotubes of the carbon nanotube-infused fibers can also be oriented such that they are substantially perpendicular to the surface of the fiber material or such that they are substantially parallel to the longitudinal axis of the fiber material. In the present embodiments, by using carbon nanotube-infused fibers having substantially perpendicular carbon nanotubes, a better exposure of an electrolyte to the carbon nanotube surface area can be realized. This is particularly true, when the carbon nanotubes are present in a substantially unbundled state. The above-referenced methods for preparing carbon nanotube-infused fibers are particularly adept at achieving a substantially perpendicular orientation and a substantially unbundled state, thereby providing carbon nanotube-infused fibers having a high effective surface area for use in the present embodiments. Additional details concerning the carbon nanotube-infused fibers and methods for production thereof are set forth hereinafter.

Not only can carbon nanotubes replace activated carbon particles in supercapacitor embodiments of the present electrical devices, but the carbon nanotube-infused fibers become indistinct from the electrode itself in such cases. In conventional supercapacitors containing activated carbon particles, there are electrode plates that are in contact with the activated carbon particles (see FIG. 1). In the present supercapacitor embodiments, the carbon nanotube-infused fibers are not in contact with a separate electrode plate, thereby making the electrodes the carbon nanotube-infused fibers themselves. This feature represents a new paradigm in supercapacitor design. In addition, the design of the present supercapacitor embodiments allows multiple electrode layers to be incorporated therein, thereby further increasing the amount of electrical energy that can be stored. Depending on the size of the continuous fibers and the length, diameter, and coverage density of carbon nanotubes thereon, effective electrode surface areas can be realized that are up to about 14,000 times that of conventional supercapacitors containing activated carbon particles. As previously noted, all of these parameters can be readily varied in the preparation of carbon nanotube-infused fibers and can be used to tune the present supercapacitor embodiments to a desired capacitance.

As used herein, the terms “fiber,” “fiber material,” or “filament” equivalently refer to any material that has a fibrous component as a basic structural feature. As used herein, the term “continuous fibers” refers to spoolable lengths of fiber materials such as individual filaments, yarns, rovings, tows, tapes, ribbons, woven and non-woven fabrics, plies, mats, and the like.

As used herein, the terms “spoolable lengths” or “spoolable dimensions” equivalently refer to a fiber material that has at least one dimension that is not limited in length, thereby allowing the fiber material to be stored on a spool or mandrel following infusion with carbon nanotubes. A fiber material of “spoolable lengths” or “spoolable dimensions” has at least one dimension that indicates the use of either batch or continuous processing for carbon nanotube infusion thereon.

As used herein, the term “infused” refers to being bonded and “infusion” refers to the process of bonding. As used herein, the terms “carbon nanotube-infused fiber” or “carbon nanotube-infused fiber material” equivalently refer to a fiber material that has carbon nanotubes bonded thereto. Such bonding of carbon nanotubes to a fiber material can involve mechanical attachment, covalent bonding, ionic bonding, pi-pi interactions (pi-stacking interactions), and/or van der Waals force-mediated physisorption. In some embodiments, the carbon nanotubes can be directly bonded to the fiber material. In other embodiments, the carbon nanotubes can be indirectly bonded to the fiber material via a barrier coating and/or catalytic nanoparticles used to mediate growth of the carbon nanotubes. The particular manner in which the carbon nanotubes are infused to the fiber material can be referred to as the bonding motif.

As used herein, the term “nanoparticle” refers to particles having a diameter between about 0.1 nm and about 100 nm in equivalent spherical diameter, although nanoparticles need not necessarily be spherical in shape. As used herein, the term “catalytic nanoparticle” refers to a nanoparticle that possesses catalytic activity for mediating carbon nanotube growth.

As used herein, the term “transition metal” refers to any element or alloy of elements in the d-block of the periodic table (Groups 3 through 12), and the term “transition metal salt” refers to any transition metal compound such as, for example, transition metal oxides, carbides, nitrides, and the like. Illustrative transition metals that form catalytic nanoparticles suitable for synthesizing carbon nanotubes include, for example, Ni, Fe, Co, Mo, Cu, Pt, Au, Ag, alloys thereof, salts thereof, and mixtures thereof.

As used herein, the terms “sizing agent,” or “sizing,” collectively refer to materials used in the manufacture of fiber materials as a coating to protect the integrity of the fiber material, to provide enhanced interfacial interactions between the fiber material and a matrix material, and/or to alter and/or to enhance certain physical properties of the fiber material.

As used herein, the term “uniform in length” refers to a condition in which carbon nanotubes have lengths with tolerances of plus or minus about 20% or less of the total carbon nanotube length, for carbon nanotube lengths ranging from about 1 μm to about 500 μm. At very short carbon nanotube lengths (e.g., about 1 μm to about 4 μm), the tolerance can be plus or minus about 1 μm, that is, somewhat more than about 20% of the total carbon nanotube length.

As used herein, the term “uniform in density distribution” refers to a condition in which the carbon nanotube coverage density on a fiber material has a tolerance of plus or minus about 10% over the fiber material surface area that is covered with carbon nanotubes.

As used herein, the term “continuous process” refers to a multi-stage process that operates in a substantially uninterrupted manner, particularly a process for producing carbon nanotube-infused fibers.

In some embodiments, electrical devices described herein include a first electrode layer and a second electrode layer, where the first electrode layer and the second electrode layer contain a plurality of continuous fibers that are infused with carbon nanotubes. In some embodiments, the electrical devices are supercapacitors.

In some embodiments, the electrical devices further include a base plate, an electrolyte in contact with the first electrode layer and the second electrode layer, and a layer of separator material disposed between the first electrode layer and the second electrode layer, where the separator material is permeable to ions of the electrolyte. In some embodiments, the plurality of continuous fibers of the first electrode layer are conformally wound about the base plate, and the plurality of continuous fibers of the second electrode layer are conformally wound about the layer of separator material.

The types of carbon nanotubes infused to the continuous fibers can generally vary without limitation. In various embodiments, the carbon nanotubes infused to the continuous fibers can be, for example, any of a number of cylindrically-shaped carbon allotropes of the fullerene family including single-wall carbon nanotubes, double-wall carbon nanotubes, multi-wall carbon nanotubes, and any combination thereof. In some embodiments, the carbon nanotubes can be capped with a fullerene-like structure. Stated another way, the carbon nanotubes have closed ends in such embodiments. However, in other embodiments, the carbon nanotubes can remain open-ended. In some embodiments, closed carbon nanotube ends can be opened through treatment with an appropriate oxidizing agent (e.g., HNO₃/H₂SO₄). In some embodiments, the carbon nanotubes can encapsulate other materials. In some embodiments, the carbon nanotubes can be covalently functionalized after becoming infused to the fiber material. In some embodiments, a plasma process can be used to promote functionalization of the carbon nanotubes.

Carbon nanotubes can be metallic, semimetallic or semiconducting depending on their chirality. An established system of nomenclature for designating a carbon nanotube's chirality is recognized by those of ordinary skill in the art and is distinguished by a double index (n,m), where n and m are integers that describe the cut and wrapping of hexagonal graphite when formed into a tubular structure. In addition to chirality, a carbon nanotube's diameter also influences its electrical conductivity and the related property of thermal conductivity. In the synthesis of carbon nanotubes, the carbon nanotubes' diameters can be controlled by using catalytic nanoparticles of a given size. Typically, a carbon nanotube's diameter is approximately that of the catalytic nanoparticle that catalyzes its formation. Therefore, carbon nanotubes' properties can be controlled in one respect by adjusting the size of the catalytic nanoparticles used in their synthesis, for example. By way of non-limiting example, catalytic nanoparticles having a diameter of about 1 nm can be used to infuse a fiber material with single-wall carbon nanotubes. Larger catalytic nanoparticles can be used to prepare predominantly multi-wall carbon nanotubes, which have larger diameters because of their multiple nanotube layers, or mixtures of single-wall and multi-wall carbon nanotubes. Multi-wall carbon nanotubes typically have a more complex conductivity profile than do single-wall carbon nanotubes due to interwall reactions that can occur between the individual nanotube layers and redistribute current non-uniformly. By contrast, there is no change in current across different portions of a single-wall carbon nanotube.

In general, the carbon nanotubes infused to the continuous fibers can be of any length. Longer carbon nanotubes are generally more advantageous in the present supercapacitor embodiments, since they can provide electrodes having a higher effective surface area. In various embodiments, the carbon nanotubes can have a length ranging between about 1 μm and about 1000 μm or between about 1 μm and about 500 μm. In some embodiments, the carbon nanotubes can have a length ranging between about 100 μm and about 500 μm. In other embodiments, the carbon nanotubes can have a length ranging between about 1 μm and about 50 μm or between about 10 μm and about 25 μm. In some embodiments, the carbon nanotubes can be substantially uniform in length.

In some embodiments, an average length of the carbon nanotubes ranges between about 1 μm and about 500 μm, including about 1 μm, about 2 μm, about 3 μm, about 4 μm, about 5 about 6 μm, about 7 μm, about 8 μm, about 9 μm, about 10 μm, about 15 μm, about 20 μm, about 25 μm, about 30 μm, about 35 μm, about 40 μm, about 45 μm, about 50 μm, about 60 μm, about 70 μm, about 80 μm, about 90 μm, about 100 μm, about 150 μm, about 200 μm, about 250 μm, about 300 μm, about 350 μm, about 400 μm, about 450 μm, about 500 μm, and all values and subranges therebetween. In some embodiments, an average length of the carbon nanotubes is less than about 1 μm, including about 0.5 μm, for example, and all values and subranges therebetween. In some embodiments, an average length of the carbon nanotubes ranges between about 1 μm and about 10 including, for example, about 1 μm, about 2 μm, about 3 μm, about 4 μm, about 5 μm, about 6 μm, about 7 μm, about 8 μm, about 9 μm, about 10 μm, and all values and subranges therebetween. In still other embodiments, an average length of the carbon nanotubes is greater than about 500 μm, including, for example, about 510 μm, about 520 μm, about 550 μm, about 600 μm, about 700 μm, and all values and subranges therebetween.

The average length of the carbon nanotubes can be one factor that determines the weight percentage of carbon nanotubes infused to the continuous fiber. In general, the carbon nanotube-infused fibers described in the above-referenced, co-pending patent applications have much higher carbon nanotube loading percentages than can be obtained by other methods. For example, carbon nanotube-infused fibers can contain between about 1% to about 30% or even about 40% to about 50% infused carbon nanotubes by weight. The chosen carbon nanotube weight percentage can be dictated by the desired capacitance in the present supercapacitor embodiments.

The carbon nanotube coverage density on the continuous fibers can be another factor that determines the weight percentage of infused carbon nanotubes. In some embodiments, the carbon nanotubes infused to the fiber material are generally uniform in density distribution, referring to the uniformity of the carbon nanotube density that is infused to the fiber material. As defined above, the tolerance for a uniform density distribution is plus or minus about 10% over the fiber material surface area that is infused with carbon nanotubes. By way of non-limiting example, this tolerance is equivalent to about ±1500 carbon nanotubes/μm² for a carbon nanotube having a diameter of 8 nm and 5 walls. Such a figure assumes that the space inside the carbon nanotube is fillable. In some embodiments, the maximum carbon nanotube density, expressed as a percent coverage of the fiber material (i.e., the percentage of the fiber material surface area that is covered with carbon nanotubes) can be as high as about 55%, again assuming a carbon nanotube having an 8 nm diameter, 5 walls and fillable space within. 55% surface area coverage is equivalent to about 15,000 carbon nanotubes/μm² for a carbon nanotube having the referenced dimensions. In some embodiments, the density of coverage is up to about 15,000 carbon nanotubes/μm². One of ordinary skill in the art will recognize that a wide range of carbon nanotube density distributions can be attained by varying the disposition of the catalytic nanoparticles on the surface of the fiber material, the exposure time of the fiber material to carbon nanotube growth conditions, and the actual growth conditions themselves used to infuse the carbon nanotubes to the fiber material.

In some embodiments, the density of carbon nanotube coverage on the continuous fibers can be adjusted to account for a change in the size of the ions of an electrolyte. For example, if an electrolyte contains larger ions, a lower density of carbon nanotube coverage on the continuous fibers can be used to ensure satisfactory ion mobility and electrode contact during charge and discharge cycles of various supercapacitor embodiments.

In accordance with some of the present embodiments, a plurality of continuous fibers that are infused with carbon nanotubes form the electrode layers of a supercapacitor. The first electrode layer can be formed by winding the continuous fibers about a central base plate, and the second electrode layer and any additional electrode layers can be formed by winding the continuous fibers over the first electrode layer. A layer of separator material is disposed between the electrode layers. FIG. 2A shows an isometric schematic of the first electrode layer in an illustrative embodiment of the present supercapacitors. As shown in FIG. 2, continuous fiber 201 is conformally wound about base plate 200 to form the first electrode layer of the present supercapacitors. Terminal end 202 of continuous fiber 201 can be attached to an electrode terminal for charging or discharging the supercapacitor. The electrode terminal can be located on the base plate in some embodiments or placed elsewhere in other embodiments. FIG. 2B shows an isometric schematic of the first electrode layer in an illustrative embodiment of the present supercapacitors in which electrode terminal 204 is located on base plate 200. Continuous fiber 201 is conformally wound about base plate 200, and terminal end 202 of continuous fiber 201 is attached to electrode terminal 204. Electrode terminal 204 can optionally be electrically isolated from base plate 200 via insulator material 205, if desired. A second electrode terminal can also be included on base plate 200 for connection to the continuous fibers of other electrode layers, if desired (not shown).

Although FIGS. 2A and 2B have shown spacing between adjacent windings of continuous fiber 201, it is to be understood that the spacing depicted is for purposes of illustration clarity only. As will be evident to one of ordinary skill in the art, by having adjacent windings of continuous fiber 201 as closely spaced as possible, a larger number of carbon nanotubes per unit area can be obtained, thereby leading to higher electrode layer surface areas and a higher capacitance per unit weight of continuous fiber. It should be noted, however, that the spacing between adjacent windings of continuous fiber 201 can be varied, if needed, to provide a desired capacitance in a supercapacitor of a given size.

Although not precluded in the present embodiments, it is generally true that there is substantially no overlap between adjacent windings of continuous fiber 201, as this would produce electrode layers having a smaller surface area per unit weight of continuous fiber. Accordingly, in some embodiments, the continuous fibers of the electrode layers are substantially parallel to one another in order to avoid such overlap. However, some overlap of continuous fiber 201 in adjacent windings can be used to adjust the capacitance, if desired, as described previously for embodiments where there is spacing between adjacent windings. It should be noted that some contact between individual continuous fibers in higher order continuous fiber structures (e.g., fiber tows, fiber ribbons and/or fiber tapes) can be tolerated as long as the electrolyte has sufficient access to the surface area of the individual continuous fibers.

After formation of the first electrode layer as described above, a layer of separator material that is permeable to ions of an electrolyte can then be disposed on the first electrode layer. Subsequently, a second electrode layer can be formed on the layer of separator material by winding a separate portion of continuous fibers about the layer of separator material. Deposition of additional layers of separator material and winding of continuous fibers thereon can be conducted, if desired, to form a supercapacitor having more than two electrode layers.

FIG. 3 shows a schematic of an illustrative embodiment of the present supercapacitors as viewed parallel to the longitudinal axes of the continuous fibers of the electrode layers. Supercapacitor 300 of FIG. 3 contains two electrode layers, although more electrode layers can be added as described above. As shown in FIG. 3, supercapacitor 300 contains base plate 301 about which is wrapped continuous fiber 302 (see FIGS. 2A and 2B) having carbon nanotubes 303 infused thereon. Sections of continuous fiber 302 looping between the top and bottom of base plate 301 have been omitted for clarity. A layer of separator material 304 is disposed upon continuous fiber 302 and carbon nanotubes 303. Continuous fiber 305 having carbon nanotubes 306 infused thereon are wrapped about the layer of separator material 304. Again, sections of continuous fiber 305 looping between the top and bottom of the layer of separator 304 have been omitted for clarity. An electrolyte (not shown) is associated with continuous fibers 302 and 305 and carbon nanotubes 303 and 306 infused thereon. The layer of separator material 304 provides charge separation between the first electrode layer and the second electrode layer.

Referring still to FIG. 3, supercapacitor 300 can further include outer insulator casing 307 to contain the electrolyte therein and to provide electrical isolation. Illustrative outer insulating casings can include, for example, an insulating box containing supercapacitor 300 or an insulating shrink wrap covering supercapacitor 300. The nature of the outer insulator casing 307 can be varied according to the desired operational needs of the supercapacitor. For example, if it desired that supercapacitor 300 remains flexible or if release of the electrolyte is not a concern, a simple plastic shrink wrap outer insulator casing can be sufficient to contain the components therein. However, if supercapacitor 300 needs more mechanical support or if release of the electrolyte is a particular concern, outer insulator casing 307 can be made from a more rigid material (e.g., a plastic box).

In some embodiments, outer insulator casing 307 can be omitted. For example, by placing supercapacitor 300 (without outer insulator casing 307) in a reservoir of electrolyte, a working supercapacitor can be produced. In this case, there is an excess of electrolyte about the outermost electrode layer, which for the supercapacitor of FIG. 3 is the second electrode layer (continuous fibers 305 and carbon nanotubes 306 infused thereon). The excess of electrolyte about the second electrode layer does not significantly alter the operational principles of the supercapacitor. In these embodiments, the container for the electrolyte reservoir can be considered to be the outer insulator casing 307 of supercapacitor 300. For example, the electrolyte reservoir can be contained in a plastic bucket or like container. However, it is not required that the container for the electrolyte reservoir be an insulator in these embodiments, as the container can be electrically isolated from its environment in other ways, if desired.

In general, continuous fibers of any type that can infused with carbon nanotubes can be used in the present supercapacitors and methods for production thereof. As described above, continuous fibers such as, for example, glass fibers, carbon fibers, metal fibers, ceramic fibers, and organic fibers can be successfully infused with carbon nanotubes. Additional details concerning the carbon nanotube-infused fibers and methods for their production are set forth hereinbelow.

In various embodiments, individual continuous fibers (i.e., individual filaments) have a diameter ranging between about 1 μm and about 100 μm. Continuous length fibers having diameters in this range are readily available from a variety of commercial sources.

In some embodiments, the carbon nanotubes infused to the continuous fibers are substantially perpendicular to the surface of the continuous fibers. Although carbon nanotube-infused fibers can be produced such that they have the infused carbon nanotubes present in any desired orientation, one of ordinary skill in the art will recognize that a substantially perpendicular orientation will maximize the carbon nanotube surface area and, hence, the electrode layer surface area. For at least this reason, a substantially perpendicular orientation of the carbon nanotubes is advantageous in the present embodiments.

In some embodiments, the continuous fibers can be electrically conductive before being infused with carbon nanotubes. Illustrative conductive fibers that can be used in the present embodiments include, for example, carbon fibers and metal fibers (e.g., stainless steel, aluminum, copper and the like). Although carbon nanotube infusion to the continuous fibers imparts electrical conductivity thereto, better current collection and charge storage properties are generally observed when the continuous fibers are initially electrically conductive before carbon nanotube infusion. In alternative embodiments, however, the continuous fibers can be non-conductive before being infused with carbon nanotubes. In such embodiments, a conductivity enhancer can be used in association with the continuous fibers in order to enhance current collection and charge storage. For example, a metal form such as metal foils, metal ribbons, metal powders, and/or metal nanoparticles can be included with the continuous fibers in the present embodiments. In such embodiments, the metal nanoparticles can include residual catalytic nanoparticles used for mediating carbon nanotube growth. Such conductivity enhancers can also be used when the continuous fibers are conductive as well. In some embodiments, the present electrical devices further contain a conductivity enhancer associated with the first electrode layer and the second electrode layer, where the conductivity enhancer includes at least one metal form such as, for example, metal foils, metal ribbons, metal powders, metal nanoparticles, and the like.

In general, the continuous fibers are used in a higher order fiber form in the present embodiments, rather than being placed therein as individual filaments. Such higher order fiber forms vary widely in structure and are considered in further detail immediately hereinafter. In some embodiments, the fiber form of the continuous fibers can be, for example, a fiber tow, a fiber tape, and/or a fiber ribbon. In other embodiments, the fiber form can be, for example, a fiber roving, a yarn, a fiber braid, a woven or non-woven fabric, a fiber ply, and/or a fiber mat. In some embodiments, the individual filaments are substantially parallel to one another in the higher order fiber form. In some embodiments, the continuous fibers are substantially parallel to one another in the first electrode layer and the second electrode layer. In some embodiments, there is substantially no overlap of the continuous fibers in adjacent windings about the base plate and the layer(s) of separator material when used in supercapacitors.

Rovings include soft strands of continuous fiber that have been twisted, attenuated and freed of foreign matter.

Fiber tows are generally compactly associated bundles of continuous fibers, which can be twisted together to give yarns in some embodiments. Yarns include closely associated bundles of twisted fibers, wherein each fiber diameter in the yarn is relatively uniform. Yarns have varying weights described by their ‘tex,’ (expressed as weight in grams per 1000 linear meters), or ‘denier’ (expressed as weight in pounds per 10,000 yards). For yarns, a typical tex range is usually between about 200 and about 2000.

Fiber braids are rope-like structures of densely packed continuous fibers. Such rope-like structures can be assembled from yarns, for example. Braided structures can optionally include a hollow portion. Alternately, a braided structure can be assembled about another core material.

Fiber tows can also include associated bundles of untwisted continuous fibers. Thus, fiber tows are a convenient form for manipulating large quantities of substantially parallel fibers in a single operation. As in yarns, the individual fiber diameters in a fiber tow are generally uniform. Fiber tows also have varying weights and a tex range that is usually between about 200 and 2000. In addition, fiber tows are frequently characterized by the number of thousands of individual fibers in the fiber tow, such as, for example, a 12K tow, a 24K tow, a 48K tow, and the like.

Tapes and ribbons contain continuous fibers that can be assembled as weaves or as non-woven flattened fiber tows, for example. Tapes can vary in width and are generally two-sided structures similar to a ribbon. As described in Applicants' co-pending patent applications, carbon nanotubes can be infused to a tape on one or both sides of the tape. Further, carbon nanotubes of different types, diameters or lengths can be grown on each side of a tape.

In some embodiments, the continuous fibers can be organized into fabric or sheet-like structures. These include, for example, woven fabrics, non-woven fabrics, non-woven fiber mats and fiber plies, in addition to the tapes described above. Such higher ordered structures can be assembled from parent continuous fibers, fiber tows, yarns, or the like.

The identity of base plate of the present supercapacitor embodiments is not particularly limited. In some embodiments, the base plate is an insulator material (e.g., a non-conductive material). In such embodiments, the role of the base plate is primarily structural and provides a support for building the present supercapacitors thereon. Such non-conductive base plates can vary over a wide composition range and include, for example, plastics, ceramics, aluminum oxide, silicon oxide, and wood. The rigidity and mechanical strength of the base plate can be adjusted for a given application. For example, it can be desirable for the base plate to be flexible in some embodiments, such that supercapacitor itself maintains some degree of flexibility. Likewise, if the supercapacitor is intended for an application in which payload weight is a concern, for example, a lightweight base plate can be used (e.g., a foamed polyurethane or polystyrene). In alternative embodiments, the base plate can be an electrical conductor, if desired. In embodiments in which the base plate is electrically conductive, it can particularly augment the current collection properties of the first electrode layer.

The dimensions of the base plate are not particularly limited, except that the base plate should be capable of mechanically supporting the supercapacitor and its components. Ultimately, the size of the base plate determines the surface area of the electrode layers after having continuous fibers wound thereon, which produces higher capacitance values. Depending on the desired capacitance and any operational size restrictions for the resulting supercapacitor, the base plate can have a surface area ranging from about 1 cm² to about 100,000 cm². In some embodiments, the base plate is thin (e.g., a pseudo-two dimensional structure), such that at least the majority of its surface area is determined by the combined area of its top and bottom faces. For example, the base plate can have a thickness such that greater than about 95% of its surface area resides on its top and bottom faces. In other embodiments, the base plate can be a true three dimensional solid such that less than about 95% of its surface area resides on its top and bottom faces. Illustrative shapes of the base plate can include, for example, cylinders, spheres, hemispheres, triangular prisms, rectangular prisms, square prisms, rhombic prisms, trapezoidal prisms, pentagonal prisms, hexagonal prisms, heptagonal prisms, octagonal prisms, nonagonal prisms, decagonal prisms, and the like. Although the supercapacitors exemplified by FIGS. 2A, 2B and 3 have been shown with a rectangular prism base plate, it is to be understood that any of the aforementioned base plate shapes can be utilized while still operating within the spirit and scope of the present disclosure.

In some embodiments, the present electrical devices can further include an outer insulator casing. Illustrative insulator casings include, for example, plastics and wax. In some embodiments, the outer insulator casing can be a shrink wrap material (e.g., a plastic shrink wrap). In general, any dielectric material can be used to provide electrical isolation for the electrical devices and to contain the various components therein. When there are two electrode layers, the outer insulator casing can be disposed about the second electrode layer. When there are additional electrode layers, the outer insulator casing case be disposed about the outermost electrode layer. In supercapacitor embodiments where an outer insulator casing is present, a first portion of the electrolyte resides between the base plate and the layer of separator material, and a second portion of the electrolyte resides between the layer of separator material and the outer insulator casing. As noted previously, the outer insulator casing can optionally be omitted such as, for example, when the supercapacitor is placed in a reservoir of electrolyte that contacts the electrode layers in some manner. That is, in such supercapacitor embodiments, the base plate, the first electrode layer, the second electrode layer, and the layer of separator material reside in a reservoir of the electrolyte.

In some embodiments, the outer insulator casing has a thickness ranging between about 100 μm and about 10 cm. In other embodiments, the outer insulator casing has a thickness ranging between about 5 mm and about 5 cm or between about 1 cm and about 4 cm. In still other embodiments, the outer insulator casing has a thickness ranging between 10 μm and about 1 mm or between about 100 μm and about 1 mm. In general, the outer insulator casing is made as thin as possible to provide electrical isolation of the electrical device while still maintaining structural integrity thereof. As one of ordinary skill in the art will recognize, thin outer insulator casings keep material costs lower and allow lower weight supercapacitors and other electrical devices to be produced.

As previously described, the present electrical devices can further include electrode terminals to which the continuous fibers of at least the first electrode layer and the second electrode layer are connected. In some embodiments, the present electrical devices further include a first electrode terminal connected to the plurality of continuous fibers of the first electrode layer and a second electrode terminal connected to the continuous fibers of the second electrode layer. In embodiments where additional electrode layers are present, a corresponding number of additional electrode terminals can be included as well. When present, the electrode terminals can be located on the base plate in some embodiments. In embodiments where the base plate is electrically conductive, the electrode terminals can be electrically isolated from the base plate by an insulator material. In alternative embodiments, the electrode terminals can be located off the base plate. For example, the electrode terminals can be located on the outer insulator casing, if desired. In still other embodiments, the continuous fibers of the first electrode layer, the second electrode layer, and additional electrode layers, if present, can be connected directly to an electrical power source and/or electrical load without being connected thereto through intervening electrode terminals.

The layer of separator material in the present supercapacitor embodiments can be formed from any material of sufficient thickness that is capable of maintaining charge separation of the ions of the electrolyte once the supercapacitor is in a charged state. In general, the separator material is a thin film dielectric substance that is porous in nature and allows for high ion mobility between the electrode layers when the supercapacitor is charging or discharging but is capable of maintaining charge separation once the supercapacitor reaches a charged state. Thus, the layer of separator material is selectively permeable to movement of charge carriers across it. In some embodiments, the separator material can be a non-woven polymer fabric such as, for example, polyethylene non-woven fabrics, polypropylene non-woven fabrics, polyester non-woven fabrics, and polyacrylonitrile non-woven fabrics. In other embodiments, the separator material can be a porous substance such as, for example, a porous poly(vinylidene fluoride)-hexafluoropropane copolymer film, a porous cellulose film, kraft paper, rayon woven fabrics, and the like. Generally, any separator material that can be used in batteries can also be used in the present supercapacitors.

The degree of porosity of the separator material is such that the ions of the electrolyte are sufficiently mobile so as to move across the separator material when the supercapacitor is being charged or discharged but sufficiently immobile so as to maintain charge separation once the supercapacitor reaches a charged state. In some embodiments, the porosity of the separator material is greater than about 90%. In some embodiments, the porosity of the separator material ranges between about 90% and about 95%. In other embodiments, the porosity of the separator material ranges between about 90% and about 40%, or between about 87% and about 50%, or between about 85% and about 65%.

In addition to porosity, the thickness of the separator material can govern the degree of ion mobility across the separator material. For a given porosity, a thicker layer of separator material provides greater charge separation and lower ion mobility than does a thinner layer of separator material. In some embodiments, the thickness of the layer of separator material is less than about 100 μm. In some embodiments, the thickness of the layer of separator material ranges between about 100 μm and about 50 μm. In some embodiments, the thickness of the layer of separator material ranges between about 50 μm and about 25 μm or between about 25 μm and about 10 μm. In some embodiments, the thickness of the layer of separator material is less than about 10 μm. In some embodiments, the thickness of the layer of separator material ranges between about 10 μm and about 1 μm. In some embodiments, the thickness of the layer of separator material is less than about 1 μm. In some embodiments, the thickness of the layer of separator material ranges between about 100 nm and about 1 μm. In some embodiments, a thickness of the layer of separator material can be optimized to achieve a balance between electrolyte volume and voltage standoff capability.

In one embodiment, a suitable separator material can be a high porosity (e.g., >90%) polypropylene and/or polyethylene electrolytic membrane. Such electrolytic membranes are available from Celgard LLC of Charlotte, N.C. These electrolytic membranes exhibit a high electric voltage standoff capability, thereby permitting a thinner and lighter film for isolating the electrode layers. In some embodiments, a paper separator material (e.g., kraft paper) can also be used.

The electrolyte of the present supercapacitor embodiments is not particularly limited. In some embodiments, the electrolyte can be an inorganic electrolyte. In other embodiments, the electrolyte can be an organic electrolyte. As one of ordinary skill in the art will recognize, aqueous electrolytes offer low internal resistance values but have a working range limited to about 1 V. In contrast, organic electrolytes have a working voltage range of up to about 2.5 V or about 3 V but have a higher internal resistance. As with other components of the present supercapacitor embodiments, the electrolyte identity and concentration can be altered to account for different end uses

Illustrative aqueous electrolytes include aqueous acid solutions (e.g., sulfuric acid, phosphoric acid, hydrochloric acid, and the like), aqueous base solutions (e.g., sodium hydroxide or potassium hydroxide), and neutral solutions. Neutral electrolyte solutions are generally formed by dissolving a salt in an aqueous medium. Illustrative salts that are suitable for use as neutral electrolytes include, for example, sodium chloride, potassium chloride, sodium oxide, potassium oxide, sodium sulfate, potassium sulfate, and the like. Additional aqueous electrolytes can be envisioned by those of ordinary skill in the art. In general, the concentration of the aqueous electrolyte ranges between about 0.1 and 20 M or between about 1 wt. % and 100 wt. %.

Organic electrolytes include an electrolytic species dissolved in an organic solvent. Illustrative electrolytic species include, for example, tetraalkylammonium salts (e.g., tetraethylammonium or tetramethylammonium halides and hydroxides); quaternary phosphonium salts; and lithium, sodium or potassium tetrafluoroborates, perchlorates, hexafluorophosphates, bis(trifluoromethane)sulfonates, bis(trifluoromethane)sulfonylimides, or tris(trifluoromethane)sulfonylmethides. In general, the concentration of the electrolytic species in the organic solvent ranges between about 0.1 M and about 5 M or between about 0.5 M and about 3 M.

Organic solvents used in organic electrolytes are generally aprotic organic solvents having a high dielectric constant. Illustrative organic solvents that can be used in an organic electrolyte include, without limitation, alkyl carbonates (e.g., propylene carbonate, ethylene carbonate, butylene carbonate, dimethyl carbonate, diethyl carbonate, dipropyl carbonate, methyl ethyl carbonate, methyl butyl carbonate, methyl propyl carbonate, ethyl propyl carbonate, butyl propyl carbonate, 1,2-butylene carbonate, 2,3-butylene carbonate, 1,2-pentene carbonate, and 2,3-pentene carbonate), nitriles (e.g., acetonitrile, acrylonitrile, propionitrile, butyronitrile and benzonitrile), sulfoxides (e.g., dimethyl sulfoxide, diethyl sulfoxide, ethyl methyl sulfoxide, and benzylmethyl sulfoxide), amides (e.g., formamide, methylformamide, and dimethylformamide), pyrrolidones (e.g., N-methylpyrrolidone), lactones (e.g., γ-butyrolactone, γ-valerolactone, 2-methyl-γ-butyrolactone, and acetyl-γ-butyrolactone), phosphate triesters, nitromethane, ethers (e.g., 1,2-dimethoxyethane; 1,2-diethoxyethane; 1,2-methoxyethoxyethane; 1,2- or 1,3-dimethoxypropane; 1,2- or 1,3-diethoxypropane; 1,2- or 1,3-ethoxymethoxypropane; 1,2-dibutoxyethane; tetrahydrofuran; 2-methyltetrahydrofuran and other alkyl, dialkyl, alkoxy or dialkoxy tetrahydrofurans; 1,4-dioxane; 1,3-dioxolane; 1,4-dioxolane; 2-methyl-1,3-dioxolane; 4-methyl-1,3-dioxolane; sulfolane; 3-methylsulfolane; methyl ether; ethyl ether; propyl ether; diethylene glycol dialkyl ether; triethylene glycol dialkyl ethers; ethylene glycol dialkyl ethers; and tetraethylene glycol dialkyl ethers), esters (e.g., alkyl propionates such as methyl or ethyl propionate, dialkyl malonates such as diethyl malonate, alkyl acetates such as methyl acetate and ethyl acetate, and alkyl formates such as methyl formate and ethyl formate); and maleic anhydride. In addition, organic gels and the like can be used, if desired.

In some embodiments, the electrolyte can be an ionic liquid such as, for example, benzyldimethylpropylammonium aluminum tetrachlorate, benzyldimethylammonium imide, ethylmethylammonium bisulfate, 1-butyl-3-methylimidazolium tetrafluoroborate, or tetraethylammonium tetrafluoroborate. Any of the above organic solvents can optionally be used in combination with such ionic liquids.

In various embodiments, the present electrical devices can contain more than two electrode layers. In some embodiments, the electrical devices further contain at least one additional layer of separator material and at least one additional electrode layer containing a plurality of continuous fibers that are infused with carbon nanotubes. In such embodiments, each electrode layer is separated from one another by a layer of separator material. Further, the electrolyte is in contact with each electrode layer in such embodiments. By repeating the electrode and separator material layering, a supercapacitor having any number of desired layers can be formed. For example, a supercapacitor weighing tens to hundreds of pounds and having a capacitance of several thousand Farads can be obtained by repeating the electrode layering.

Capacitance values of the present supercapacitor embodiments can vary over a wide range. In various embodiments, the supercapacitors of the present disclosure can have a capacitance ranging between about 0.5 Farad/gram of continuous fibers and about 500 Farad/gram of continuous fibers. In some embodiments, the supercapacitors have a capacitance ranging between about 1 Farad/gram of continuous fibers and about 250 Farad/gram of continuous fibers. In still other embodiments, the supercapacitors have a capacitance ranging between about 2 Farad/gram of continuous fibers and about 100 Farad/gram of continuous fibers. In some embodiments, the supercapacitors have a capacitance of at least about 1 Farad/gram of continuous fibers. In other embodiments, the supercapacitors have a capacitance of at least about 2 Farad/gram of continuous fibers. It should be noted that the foregoing values are for supercapacitors having only two electrode layers. When the supercapacitors have more than two electrode layers, the capacitance increases in substantially direct proportion to the number of additional electrode layers. That is, a supercapacitor having three electrode layers has about twice the capacitance of a supercapacitor having only two electrode layers. In addition, the supercapacitors can be used singly or stacked in series.

FIG. 4 shows a schematic of a coin press sample supercapacitor structure. Such a supercapacitor structure can be readily prepared for testing of the supercapacitors described herein by connecting outer portion 400 and inner portion 401 to form supercapacitor 402. FIG. 5 shows an illustrative cyclic voltammogram of a supercapacitor of the present disclosure.

In some embodiments, methods described herein include providing a plurality of continuous fibers that are infused with carbon nanotubes, forming a first electrode layer from a first portion of the plurality of continuous fibers, and forming a second electrode layer from a second portion of the plurality of continuous fibers.

In some embodiments, the methods further include exposing the first electrode layer and the second electrode layer to an electrolyte, and applying a layer of separator material between the first electrode layer and the second electrode layer, where the separator material is permeable to ions of the electrolyte. In some embodiments, forming a first electrode layer involves winding the first portion of the plurality of continuous fibers conformally about a base plate, and forming a second electrode layer involves winding the second portion of the plurality of continuous fibers conformally over the first electrode layer. In some embodiments, winding to form the first electrode layer, winding to form the second electrode layer, and applying the layer of separator material can all occur simultaneously. In other embodiments, each layer can be wound or applied separately.

In some embodiments, the methods further include applying at least one additional layer of separator material over the second electrode layer and winding at least one additional electrode layer over the second electrode layer. In such embodiments, the at least one additional electrode layer contains a plurality of continuous fibers that are infused with carbon nanotubes, and each electrode layer is separated from one another by a layer of separator material. Further, the electrolyte is in contact with each electrode layer.

In other embodiments, methods described herein include providing a plurality of continuous fibers that are infused with carbon nanotubes, forming a first electrode layer by winding a portion of the plurality of continuous fibers conformally about a base plate, and forming at least two additional electrode layers over the first electrode layer by winding separate portions of the plurality of continuous fibers conformally over the first electrode layer.

In some embodiments, the methods further include exposing the first electrode layer and the at least two additional electrode layers to an electrolyte, and applying a layer of separator material between each electrode layer, where the separator material is permeable to ions of the electrolyte.

In some embodiments, the plurality of continuous fibers are in a fiber form such as, for example, a fiber tow, a fiber tape, and/or a fiber ribbon. In some embodiments, the plurality of continuous fibers are substantially parallel to one another in the electrode layers. In some embodiments, the individual filaments of the plurality of continuous fibers are substantially parallel to one another in the fiber form. In further embodiments, there is substantially no overlap of the plurality of continuous fibers in adjacent windings of the electrode layers. In addition, when there are additional electrode layers, there can also be substantially no overlap in those layers as well. Optionally, there can be spacing between adjacent windings, if desired.

In some embodiments, the first electrode layer is exposed to the electrolyte before applying the layer of separator material. However, since the layer of separator material is permeable to the ions of the electrolyte, the first electrode layer can also be exposed to the electrolyte at a later stage of fabrication in alternative embodiments. In some embodiments, the first electrode layer, the second electrode layer, and additional electrode layers, if present, can be simultaneously exposed to the electrolyte. In some embodiments, the first electrode layer, the second electrode layer, and additional electrode layers, if present, can be simultaneously exposed to the electrolyte by simultaneous immersion in a reservoir of the electrolyte.

In some embodiments, the methods further include applying an outer insulator casing to the electrode layers. Additional details concerning the outer insulator casing have been set forth hereinabove.

Embodiments disclosed herein utilize carbon nanotube-infused fibers that can be readily prepared by methods described in commonly-owned, co-pending U.S. patent application Ser. Nos. 12/611,073, 12/611,101, 12/611,103, and 12/938,328 each of which is incorporated by reference herein in its entirety. A brief description of the processes described therein follows.

To infuse carbon nanotubes to a fiber material, the carbon nanotubes are synthesized directly on the fiber material. In some embodiments, this is accomplished by first disposing a carbon nanotube-forming catalyst (e.g., catalytic nanoparticles) on the fiber material. A number of preparatory processes can be performed prior to this catalyst deposition.

In some embodiments, the fiber material can be optionally treated with a plasma to prepare the fiber surface to accept the catalyst. For example, a plasma treated glass fiber material can provide a roughened glass fiber surface in which the carbon nanotube-forming catalyst can be deposited. In some embodiments, the plasma also serves to “clean” the fiber surface. The plasma process for “roughing” the fiber surface thus facilitates catalyst deposition. The roughness is typically on the scale of nanometers. In the plasma treatment process craters or depressions are formed that are nanometers deep and nanometers in diameter. Such surface modification can be achieved using a plasma of any one or more of a variety of different gases, including, without limitation, argon, helium, oxygen, ammonia, nitrogen and hydrogen.

In some embodiments, where a fiber material being employed has a sizing material associated with it, such sizing can be optionally removed prior to catalyst deposition. Optionally, the sizing material can be removed after catalyst deposition. In some embodiments, sizing material removal can be accomplished during carbon nanotube synthesis or just prior to carbon nanotube synthesis in a pre-heat step. In other embodiments, some sizing materials can remain throughout the entire carbon nanotube synthesis process.

Yet another optional step prior to or concomitant with deposition of the carbon nanotube-forming catalyst (i.e., catalytic nanoparticles) is application of a barrier coating on the fiber material. Barrier coatings are materials designed to protect the integrity of sensitive fiber materials, such as carbon fibers, organic fibers, glass fibers, metal fibers, and the like. Such a barrier coating can include, for example, an alkoxysilane, an alumoxane, alumina nanoparticles, spin on glass and glass nanoparticles. For example, in an embodiment the barrier coating is Accuglass T-11 Spin-On Glass (Honeywell International Inc., Morristown, N.J.). The carbon nanotube-forming catalyst can be added to the uncured barrier coating material and then applied to the fiber material together, in one embodiment. In other embodiments, the barrier coating material can be added to the fiber material prior to deposition of the carbon nanotube-forming catalyst. In such embodiments, the barrier coating can be partially cured prior to catalyst deposition. The barrier coating material can be of a sufficiently thin thickness to allow exposure of the carbon nanotube-forming catalyst to the carbon feedstock gas for subsequent CVD- or like carbon nanotube growth. In some embodiments, the barrier coating thickness is less than or about equal to the effective diameter of the carbon nanotube-forming catalyst. Once the carbon nanotube-forming catalyst and the barrier coating are in place, the barrier coating can be fully cured. In some embodiments, the thickness of the barrier coating can be greater than the effective diameter of the carbon nanotube-forming catalyst so long as it still permits access of carbon nanotube feedstock gases to the sites of the catalyst. Such barrier coatings can be sufficiently porous to allow access of carbon feedstock gases to the carbon nanotube-forming catalyst.

In some embodiments, the thickness of the barrier coating ranges between about 10 nm and about 100 nm. In other embodiments, the thickness of the barrier coating ranges between about 10 nm and about 50 nm, including 40 nm. In some embodiments, the thickness of the barrier coating is less than about 10 nm, including about 1 nm, about 2 nm, about 3 nm, about 4 nm, about 5 nm, about 6 nm, about 7 nm, about 8 nm, about 9 nm, and about 10 nm, including all values and subranges therebetween.

Without being bound by theory, the barrier coating can serve as an intermediate layer between the fiber material and the carbon nanotubes and mechanically infuses the carbon nanotubes to the fiber material. Such mechanical infusion via a barrier coating provides a robust system for carbon nanotube growth in which the fiber material serves as a platform for organizing the carbon nanotubes, while still allowing the beneficial carbon nanotube properties to be conveyed to the fiber material. Moreover, benefits of including a barrier coating include, for example, protection of the fiber material from chemical damage due to moisture exposure and/or thermal damage at the elevated temperatures used to promote carbon nanotube growth.

As described further below, the carbon nanotube-forming catalyst can be prepared as a liquid solution that contains the carbon nanotube-forming catalyst as transition metal catalytic nanoparticles. The diameters of the synthesized carbon nanotubes are related to the size of the transition metal catalytic nanoparticles as described above.

Carbon nanotube synthesis can be based on a chemical vapor deposition (CVD) process or related carbon nanotube growth process which occurs at elevated temperatures. In some embodiments, the CVD-based growth process can be plasma-enhanced by providing an electric field during the growth process such that the carbon nanotube growth follows the direction of the electric field. Other illustrative carbon nanotube growth processes include, for example, micro-cavity, laser ablation, flame synthesis, arc discharge, and high pressure carbon monoxide (HiPCO) synthesis. The specific temperature is a function of catalyst choice, but can typically be in a range of about 500° C. to about 1000° C. Accordingly, carbon nanotube synthesis involves heating the fiber material to a temperature in the aforementioned range to support carbon nanotube growth.

In some embodiments, CVD-promoted carbon nanotube growth on the catalyst-laden fiber material is performed. The CVD process can be promoted by, for example, a carbon-containing feedstock gas such as acetylene, ethylene, and/or ethanol. The carbon nanotube growth processes also generally use an inert gas (e.g., nitrogen, argon, and/or helium) as a primary carrier gas. The carbon-containing feedstock gas is typically provided in a range from between about 0% to about 15% of the total mixture. A substantially inert environment for CVD growth can, be prepared by removal of moisture and oxygen from the growth chamber.

In the carbon nanotube growth process, carbon nanotubes grow at the sites of transition metal catalytic nanoparticles that are operable for carbon nanotube growth. The presence of a strong plasma-creating electric field can be optionally employed to affect carbon nanotube growth. That is, the growth tends to follow the direction of the electric field. By properly adjusting the geometry of the plasma spray and electric field, vertically aligned carbon nanotubes (i.e., perpendicular to the surface of the fiber material) can be synthesized. Under certain conditions, even in the absence of a plasma, closely-spaced carbon nanotubes can maintain a substantially vertical growth direction resulting in a dense array of carbon nanotubes resembling a carpet or forest.

Returning to the catalyst deposition process, a carbon nanotube-forming catalyst is deposited to provide a layer (typically no more than a monolayer) of catalytic nanoparticles on the fiber material for the purpose of growing carbon nanotubes thereon. The operation of depositing catalytic nanoparticles on the fiber material can be accomplished by a number of techniques including, for example, spraying or dip coating a solution of catalytic nanoparticles or by gas phase deposition, which can occur by a plasma process. Thus, in some embodiments, after forming a catalyst solution in a solvent, the catalyst can be applied by spraying or dip coating the fiber material with the solution, or combinations of spraying and dip coating. Either technique, used alone or in combination, can be employed once, twice, thrice, four times, up to any number of times to provide a fiber material that is sufficiently uniformly coated with catalytic nanoparticles that are operable for formation of carbon nanotubes. When dip coating is employed, for example, a fiber material can be placed in a first dip bath for a first residence time in the first dip bath. When employing a second dip bath, the fiber material can be placed in the second dip bath for a second residence time. For example, fiber materials can be subjected to a solution of carbon nanotube-forming catalyst for between about 3 seconds to about 90 seconds depending on the dip configuration and linespeed. Employing spraying or dip coating processes, a fiber material with a catalyst surface density of less than about 5% surface coverage to as high as about 80% surface coverage can be obtained. At higher surface densities (e.g., about 80%), the carbon nanotube-forming catalyst nanoparticles are nearly a monolayer. In some embodiments, the process of coating the carbon nanotube-forming catalyst on the fiber material produces no more than a monolayer. For example, carbon nanotube growth on a stack of carbon nanotube-forming catalyst can erode the degree of infusion of the carbon nanotubes to the fiber material. In other embodiments, transition metal catalytic nanoparticles can be deposited on the fiber material using evaporation techniques, electrolytic deposition techniques, and other processes known to those of ordinary skill in the art, such as addition of the transition metal catalyst to a plasma feedstock gas as a metal organic, metal salt or other composition promoting gas phase transport.

Because processes to manufacture carbon nanotube-infused fibers are designed to be continuous, a spoolable fiber material can be dip-coated in a series of baths where dip coating baths are spatially separated. In a continuous process in which nascent fibers are being generated de novo, such as newly formed glass fibers from a furnace, dip bath or spraying of a carbon nanotube-forming catalyst can be the first step after sufficiently cooling the newly formed fiber material. In some embodiments, cooling of newly formed glass fibers can be accomplished with a cooling jet of water which has the carbon nanotube-forming catalyst particles dispersed therein.

In some embodiments, application of a carbon nanotube-forming catalyst can be performed in lieu of application of a sizing when generating a fiber and infusing it with carbon nanotubes in a continuous process. In other embodiments, the carbon nanotube-forming catalyst can be applied to newly formed fiber materials in the presence of other sizing agents. Such simultaneous application of a carbon nanotube-forming catalyst and other sizing agents can provide the carbon nanotube-forming catalyst in surface contact with the fiber material to insure carbon nanotube infusion. In yet further embodiments, the carbon nanotube-forming catalyst can be applied to nascent fibers by spray or dip coating while the fiber material is in a sufficiently softened state, for example, near or below the annealing temperature, such that the carbon nanotube-forming catalyst is slightly embedded in the surface of the fiber material. When depositing the carbon nanotube-forming catalyst on hot glass fiber materials, for example, care should be given to not exceed the melting point of the carbon nanotube-forming catalyst, thereby causing nanoparticle fusion and loss of control of the carbon nanotube characteristics (e.g., diameter) as a result.

Carbon nanotubes infused to a fiber material can serve to protect the fiber material from conditions including, for example, moisture, oxidation, abrasion, compression and/or other environmental conditions. In this case, the carbon nanotubes themselves can act as a sizing agent. Such a carbon nanotube-based sizing agent can be applied to a fiber material in lieu of or in addition to conventional sizing agents. When present, conventional sizing agents can be applied before or after the infusion and growth of carbon nanotubes on the fiber material. Conventional sizing agents vary widely in type and function and include, for example, surfactants, anti-static agents, lubricants, siloxanes, alkoxysilanes, aminosilanes, silanes, silanols, polyvinyl alcohol, starch, and mixtures thereof. Such conventional sizing agents can be used to protect the carbon nanotubes themselves from various conditions or to convey further properties to the fiber material that are not imparted by the carbon nanotubes. In some embodiments, a conventional sizing agent can be removed from the fiber material prior to carbon nanotube growth. Optionally, a conventional sizing agent can be replaced with another conventional sizing agent that is more compatible with the carbon nanotubes or the carbon nanotube growth conditions.

The carbon nanotube-forming catalyst solution can be a transition metal nanoparticle solution of any d-block transition metal. In addition, the nanoparticles can include alloys and non-alloy mixtures of d-block metals in elemental form, in salt form, and mixtures thereof. Such salt forms include, without limitation, oxides, carbides, and nitrides, acetates, nitrates, and the like. Non-limiting illustrative transition metal nanoparticles include, for example, Ni, Fe, Co, Mo, Cu, Pt, Au, and Ag, salts thereof and mixtures thereof. Many transition metal nanoparticle catalysts are readily commercially available from a variety of suppliers, including, for example, Ferrotec Corporation (Bedford, N.H.).

Catalyst solutions used for applying the carbon nanotube-forming catalyst to the fiber material can be in any common solvent that allows the carbon nanotube-forming catalyst to be uniformly dispersed throughout. Such solvents can include, without limitation, water, acetone, hexane, isopropyl alcohol, toluene, ethanol, methanol, tetrahydrofuran (THF), cyclohexane or any other solvent with controlled polarity to create an appropriate dispersion of the carbon nanotube-forming catalytic nanoparticles therein. Concentrations of carbon nanotube-forming catalyst in the catalyst solution can be in a range from about 1:1 to about 1:10,000 catalyst to solvent.

In some embodiments, after applying the carbon nanotube-forming catalyst to the fiber material, the fiber material can be optionally heated to a softening temperature. This step can aid in embedding the carbon nanotube-forming catalyst in the surface of the fiber material to encourage seeded growth and prevent tip growth where the catalyst floats at the tip of the leading edge a growing carbon nanotube. In some embodiments heating of the fiber material after disposing the carbon nanotube-forming catalyst on the fiber material can be at a temperature between about 500° C. and about 1000° C. Heating to such temperatures, which can be used for carbon nanotube growth, can serve to remove any pre-existing sizing agents on the fiber material allowing deposition of the carbon nanotube-forming catalyst directly on the fiber material. In some embodiments, the carbon nanotube-forming catalyst can also be placed on the surface of a sizing coating prior to heating. The heating step can be used to remove sizing material while leaving the carbon nanotube-forming catalyst disposed on the surface of the fiber material. Heating at these temperatures can be performed prior to or substantially simultaneously with introduction of a carbon-containing feedstock gas for carbon nanotube growth.

In some embodiments, the process of infusing carbon nanotubes to a fiber material includes removing sizing agents from the fiber material, applying a carbon nanotube-forming catalyst to the fiber material after sizing removal, heating the fiber material to at least about 500° C., and synthesizing carbon nanotubes on the fiber material. In some embodiments, operations of the carbon nanotube infusion process include removing sizing from a fiber material, applying a carbon nanotube-forming catalyst to the fiber material, heating the fiber material to a temperature operable for carbon nanotube synthesis and spraying a carbon plasma onto the catalyst-laden fiber material. Thus, where commercial fiber materials are employed, processes for constructing carbon nanotube-infused fibers can include a discrete step of removing sizing from the fiber material before disposing the catalytic nanoparticles on the fiber material. Some commercial sizing materials, if present, can prevent surface contact of the carbon nanotube-forming catalyst with the fiber material and inhibit carbon nanotube infusion to the fiber material. In some embodiments, where sizing removal is assured under carbon nanotube growth conditions, sizing removal can be performed after deposition of the carbon nanotube-forming catalyst but just prior to or during providing a carbon-containing feedstock gas.

The step of synthesizing carbon nanotubes can include numerous techniques for forming carbon nanotubes, including, without limitation, micro-cavity, thermal or plasma-enhanced CVD techniques, laser ablation, arc discharge, flame synthesis, and high pressure carbon monoxide (HiPCO). During CVD, in particular, a sized fiber material with carbon nanotube-forming catalyst disposed thereon, can be used directly. In some embodiments, any conventional sizing agents can be removed during carbon nanotube synthesis. In some embodiments other sizing agents are not removed, but do not hinder carbon nanotube synthesis and infusion to the fiber material due to the diffusion of the carbon-containing feedstock gas through the sizing. In some embodiments, acetylene gas can be ionized to create a jet of cold carbon plasma for carbon nanotube synthesis. The plasma is directed toward the catalyst-laden fiber material. Thus, in some embodiments synthesizing carbon nanotubes on a fiber material includes (a) forming a carbon plasma; and (b) directing the carbon plasma onto the catalyst disposed on the fiber material. The diameters of the carbon nanotubes that are grown are dictated by the size of the carbon nanotube-forming catalyst. In some embodiments, a sized fiber material can be heated to between about 550° C. and about 800° C. to facilitate carbon nanotube growth. To initiate the growth of carbon nanotubes, two or more gases are bled into the reactor: an inert carrier gas (e.g., argon, helium, or nitrogen) and a carbon-containing feedstock gas (e.g., acetylene, ethylene, ethanol or methane). Carbon nanotubes grow at the sites of the carbon nanotube-forming catalyst.

In some embodiments, a CVD growth process can be plasma-enhanced. A plasma can be generated by providing an electric field during the growth process. Carbon nanotubes grown under these conditions can follow the direction of the electric field. Thus, by adjusting the geometry of the reactor, vertically aligned carbon nanotubes can be grown where the carbon nanotubes are substantially perpendicular to the surface of the fiber material (i.e., radial growth). In some embodiments, a plasma is not required for radial growth to occur about the fiber material. For fiber materials that have distinct sides such as, for example, tapes, mats, fabrics, plies, and the like, the carbon nanotube-forming catalyst can be disposed on one or both sides of the fiber material. Correspondingly, under such conditions, carbon nanotubes can be grown on one or both sides of the fiber material as well.

As described above, the carbon nanotube synthesis is performed at a rate sufficient to provide a continuous process for infusing spoolable length fiber materials with carbon nanotubes. Numerous apparatus configurations facilitate such a continuous synthesis as exemplified below.

In some embodiments, carbon nanotube-infused fiber materials can be prepared in an “all-plasma” process. In such embodiments, the fiber materials pass through numerous plasma-mediated steps to form the final carbon nanotube-infused fiber materials. The first of the plasma processes, can include a step of fiber surface modification. This is a plasma process for “roughing” the surface of the fiber material to facilitate catalyst deposition, as described above. As also described above, surface modification can be achieved using a plasma of any one or more of a variety of different gases, including, without limitation, argon, helium, oxygen, ammonia, hydrogen, and nitrogen.

After surface modification, the fiber material proceeds to catalyst application. In the present all-plasma process, this step is a plasma process for depositing the carbon nanotube-forming catalyst on the fiber material. The carbon nanotube-forming catalyst is typically a transition metal as described above. The transition metal catalyst can be added to a plasma feedstock gas as a precursor in non-limiting forms including, for example, a ferrofluid, a metal organic, a metal salt, mixtures thereof or any other composition suitable for promoting gas phase transport. The carbon nanotube-forming catalyst can be applied at room temperature in ambient environment with neither vacuum nor an inert atmosphere being required. In some embodiments, the fiber material can be cooled prior to catalyst application.

Continuing the all-plasma process, carbon nanotube synthesis occurs in a carbon nanotube-growth reactor. Carbon nanotube growth can be achieved through the use of plasma-enhanced chemical vapor deposition, wherein carbon plasma is sprayed onto the catalyst-laden fibers. Since carbon nanotube growth occurs at elevated temperatures (typically in a range of about 500° C. to about 1000° C. depending on the catalyst), the catalyst-laden fibers can be heated prior to being exposed to the carbon plasma. For the carbon nanotube infusion process, the fiber material can be optionally heated until softening occurs. After heating, the fiber material is ready to receive the carbon plasma. The carbon plasma can be generated, for example, by passing a carbon-containing feedstock gas such as, for example, acetylene, ethylene, ethanol, and the like, through an electric field that is capable of ionizing the gas. This cold carbon plasma is directed, via spray nozzles, to the fiber material. The fiber material can be in close proximity to the spray nozzles, such as within about 1 centimeter of the spray nozzles, to receive the plasma. In some embodiments, heaters can be disposed above the fiber material at the plasma sprayers to maintain the elevated temperature of the fiber material.

Another configuration for continuous carbon nanotube synthesis involves a special rectangular reactor for the synthesis and growth of carbon nanotubes directly on fiber materials. The reactor can be designed for use in a continuous in-line process for producing carbon nanotube-infused fiber materials. In some embodiments, carbon nanotubes are grown via a CVD process at atmospheric pressure and an elevated temperature in the range of about 550° C. and about 800° C. in a multi-zone reactor. The fact that the carbon nanotube synthesis occurs at atmospheric pressure is one factor that facilitates the incorporation of the reactor into a continuous processing line for carbon nanotube infusion to the fiber materials. Another advantage consistent with in-line continuous processing using such a zone reactor is that carbon nanotube growth occurs in seconds, as opposed to minutes (or longer), as in other procedures and apparatus configurations typical in the art.

Carbon nanotube synthesis reactors in accordance with the various embodiments include the following features:

Rectangular Configured Synthesis Reactors:

The cross-section of a typical carbon nanotube synthesis reactor known in the art is circular. There are a number of reasons for this including, for example, historical reasons (e.g., cylindrical reactors are often used in laboratories) and convenience (e.g., flow dynamics are easy to model in cylindrical reactors, heater systems readily accept circular tubes (e.g., quartz, etc.), and ease of manufacturing. Departing from the cylindrical convention, the present disclosure provides a carbon nanotube synthesis reactor having a rectangular cross section. The reasons for the departure include at least the following:

1) Inefficient Use of Reactor Volume.

Since many fiber materials that can be processed by the reactor are relatively planar (e.g., flat tapes, sheet-like forms, or spread tows or rovings), a circular cross-section is an inefficient use of the reactor volume. This inefficiency results in several drawbacks for cylindrical carbon nanotube synthesis reactors including, for example, a) maintaining a sufficient system purge; increased reactor volume requires increased gas flow rates to maintain the same level of gas purge, resulting in inefficiencies for high volume production of carbon nanotubes in an open environment; b) increased carbon-containing feedstock gas flow rates; the relative increase in inert gas flow for system purge, as per a) above, requires increased carbon-containing feedstock gas flow rates. Consider that the volume of an illustrative 12K glass fiber roving is about 2000 times less than the total volume of a synthesis reactor having a rectangular cross-section. In an equivalent cylindrical reactor (i.e., a cylindrical reactor that has a width that accommodates the same planarized glass fiber material as the rectangular cross-section reactor), the volume of the glass fiber material is about 17,500 times less than the volume of the reactor. Although gas deposition processes, such as CVD, are typically governed by pressure and temperature alone, volume can have a significant impact on the efficiency of deposition. With a rectangular reactor there is a still excess volume, and this excess volume facilitates unwanted reactions. However, a cylindrical reactor has about eight times that volume available for facilitating unwanted reactions. Due to this greater opportunity for competing reactions to occur, the desired reactions effectively occur more slowly in a cylindrical reactor. Such a slow down in carbon nanotube growth, is problematic for the development of continuous growth processes. Another benefit of a rectangular reactor configuration is that the reactor volume can be decreased further still by using a small height for the rectangular chamber to make the volume ratio better and the reactions even more efficient. In some embodiments disclosed herein, the total volume of a rectangular synthesis reactor is no more than about 3000 times greater than the total volume of a fiber material being passed through the synthesis reactor. In some further embodiments, the total volume of the rectangular synthesis reactor is no more than about 4000 times greater than the total volume of the fiber material being passed through the synthesis reactor. In some still further embodiments, the total volume of the rectangular synthesis reactor is less than about 10,000 times greater than the total volume of the fiber material being passed through the synthesis reactor. Additionally, it is notable that when using a cylindrical reactor, more carbon-containing feedstock gas is required to provide the same flow percent as compared to reactors having a rectangular cross section. It should be appreciated that in some other embodiments, the synthesis reactor has a cross-section that is described by polygonal forms that are not rectangular, but are relatively similar thereto and provide a similar reduction in reactor volume relative to a reactor having a circular cross section; and c) problematic temperature distribution; when a relatively small-diameter reactor is used, the temperature gradient from the center of the chamber to the walls thereof is minimal, but with increased reactor size, such as would be used for commercial-scale production, such temperature gradients increase. Temperature gradients result in product quality variations across the fiber material (i.e., product quality varies as a function of radial position). This problem is substantially avoided when using a reactor having a rectangular cross-section. In particular, when a planar substrate is used, reactor height can be maintained constant as the size of the substrate scales upward. Temperature gradients between the top and bottom of the reactor are essentially negligible and, as a consequence, thermal issues and the product-quality variations that result are avoided.

2) Gas Introduction.

Because tubular furnaces are normally employed in the art, typical carbon nanotube synthesis reactors introduce gas at one end and draw it through the reactor to the other end. In some embodiments disclosed herein, gas can be introduced at the center of the reactor or within a target growth zone, symmetrically, either through the sides or through the top and bottom plates of the reactor. This improves the overall carbon nanotube growth rate because the incoming feedstock gas is continuously replenishing at the hottest portion of the system, which is where carbon nanotube growth is most active.

Zoning.

Chambers that provide a relatively cool purge zone extend from both ends of the rectangular synthesis reactor. Applicants have determined that if a hot gas were to mix with the external environment (i.e., outside of the rectangular reactor), there would be increased degradation of the fiber material. The cool purge zones provide a buffer between the internal system and external environments. Carbon nanotube synthesis reactor configurations known in the art typically require that the substrate is carefully (and slowly) cooled. The cool purge zone at the exit of the present rectangular carbon nanotube growth reactor achieves the cooling in a short period of time, as required for continuous in-line processing.

Non-Contact, Hot-Walled, Metallic Reactor.

In some embodiments, a metallic hot-walled reactor (e.g., stainless steel) is employed. Use of this type of reactor can appear counterintuitive because metal, and stainless steel in particular, is more susceptible to carbon deposition (i.e., soot and by-product formation). Thus, most carbon nanotube synthesis reactors are made from quartz because there is less carbon deposited, quartz is easier to clean, and quartz facilitates sample observation. However, Applicants have observed that the increased soot and carbon deposition on stainless steel results in more consistent, efficient, faster, and stable carbon nanotube growth. Without being bound by theory it has been indicated that, in conjunction with atmospheric operation, the CVD process occurring in the reactor is diffusion limited. That is, the carbon nanotube-forming catalyst is “overfed;” too much carbon is available in the reactor system due to its relatively higher partial pressure (than if the reactor was operating under partial vacuum). As a consequence, in an open system—especially a clean one—too much carbon can adhere to the particles of carbon nanotube-forming catalyst, compromising their ability to synthesize carbon nanotubes. In some embodiments, the rectangular reactor is intentionally run when the reactor is “dirty,” that is with soot deposited on the metallic reactor walls. Once carbon deposits to a monolayer on the walls of the reactor, carbon will readily deposit over itself. Since some of the available carbon is “withdrawn” due to this mechanism, the remaining carbon feedstock, in the form of radicals, reacts with the carbon nanotube-forming catalyst at a rate that does not poison the catalyst. Existing systems run “cleanly” which, if they were open for continuous processing, would produce a much lower yield of carbon nanotubes at reduced growth rates.

Although it is generally beneficial to perform carbon nanotube synthesis “dirty” as described above, certain portions of the apparatus (e.g., gas manifolds and inlets) can nonetheless negatively impact the carbon nanotube growth process when soot creates blockages. In order to combat this problem, such areas of the carbon nanotube growth reaction chamber can be protected with soot inhibiting coatings such as, for example, silica, alumina, or MgO. In practice, these portions of the apparatus can be dip-coated in these soot inhibiting coatings. Metals such as INVAR® can be used with these coatings as INVAR has a similar CTE (coefficient of thermal expansion) ensuring proper adhesion of the coating at higher temperatures, preventing the soot from significantly building up in critical zones.

Combined Catalyst Reduction and Carbon Nanotube Synthesis.

In the carbon nanotube synthesis reactor disclosed herein, both catalyst reduction and carbon nanotube growth occur within the reactor. This is significant because the reduction step cannot be accomplished timely enough for use in a continuous process if performed as a discrete operation. In a typical process known in the art, a reduction step typically takes 1-12 hours to perform. Both operations occur in a reactor in accordance with the present disclosure due, at least in part, to the fact that carbon-containing feedstock gas is introduced at the center of the reactor, not the end as would be typical in the art using cylindrical reactors. The reduction process occurs as the fiber material enters the heated zone. By this point, the gas has had time to react with the walls and cool off prior to reducing the catalyst (via hydrogen radical interactions). It is this transition region where the reduction occurs. At the hottest isothermal zone in the system, carbon nanotube growth occurs, with the greatest growth rate occurring proximal to the gas inlets near the center of the reactor.

In some embodiments, when loosely affiliated fiber materials including, for example, tows or rovings are employed (e.g., a glass roving), the continuous process can include steps that spread out the strands and/or filaments of the tow or roving. Thus, as a tow or roving is unspooled it can be spread using a vacuum-based fiber spreading system, for example. When employing sized glass fiber rovings, for example, which can be relatively stiff, additional heating can be employed in order to “soften” the roving to facilitate fiber spreading. The spread fibers which contain individual filaments can be spread apart sufficiently to expose an entire surface area of the filaments, thus allowing the roving to more efficiently react in subsequent process steps. For example, a spread tow or roving can pass through a surface treatment step that is composed of a plasma system as described above. The roughened, spread fibers then can pass through a carbon nanotube-forming catalyst dip bath. The result is fibers of the glass roving that have catalyst particles distributed radially on their surface. The catalyzed-laden fibers of the roving then enter an appropriate carbon nanotube growth chamber, such as the rectangular chamber described above, where a flow through atmospheric pressure CVD or plasma enhanced-CVD process is used to synthesize carbon nanotubes at rates as high as several microns per second. The fibers of the roving, now having radially aligned carbon nanotubes, exit the carbon nanotube growth reactor.

Although the invention has been described with reference to the disclosed embodiments, one of ordinary skill in the art will readily appreciate that these only illustrative of the invention. It should be understood that various modifications can be made without departing from the spirit of the invention. 

What is claimed is:
 1. A electrical device comprising: a first electrode layer; and a second electrode layer; wherein the first electrode layer and the second electrode layer comprise adjacent windings of a plurality of continuous fibers, infused with carbon nanotubes, wound about a base plate.
 2. The electrical device of claim 1, further comprising: a layer of separator material disposed between the first electrode layer and the second electrode layer; wherein the separator material is permeable to ions of an electrolyte; and an electrolyte in contact with the first electrode layer and the second electrode layer.
 3. The electrical device of claim 2, wherein the plurality of continuous fibers of the first electrode layer are conformally wound about the base plate and the plurality of continuous fibers of the second electrode layer are conformally wound about the layer of separator material.
 4. The electrical device of claim 3, wherein there is substantially no overlap of the plurality of continuous fibers in adjacent windings about the base plate and the layer of separator material.
 5. The electrical device of claim 3, further comprising: at least one additional layer of separator material; and at least one additional electrode layer comprising a plurality of continuous fibers that are infused with carbon nanotubes; wherein each electrode layer is separated from one another by a layer of separator material; and wherein the electrolyte is in contact with each electrode layer.
 6. The electrical device of claim 5, further comprising: an outer insulator casing.
 7. The electrical device of claim 2, wherein the base plate, the first electrode layer, the second electrode layer, and the layer of separator material reside in a reservoir of the electrolyte.
 8. The electrical device of claim 2, further comprising: a first electrode terminal connected to the plurality of continuous fibers of the first electrode layer; and a second electrode terminal connected to the plurality of continuous fibers of the second electrode layer.
 9. The electrical device of claim 8, wherein the first electrode terminal and the second electrode terminal are located on the base plate.
 10. The electrical device of claim 1, wherein the plurality of continuous fibers comprise a fiber form selected from the group consisting of a fiber tow, a fiber tape, a fiber ribbon, and combinations thereof.
 11. The electrical device of claim 1, wherein the plurality of continuous fibers are substantially parallel to one another in the first electrode layer and the second electrode layer.
 12. The electrical device of claim 1, wherein the continuous fibers are electrically conductive before being infused with carbon nanotubes.
 13. The electrical device of claim 12, wherein the continuous fibers comprise continuous metal fibers.
 14. The electrical device of claim 12, wherein the continuous fibers comprise continuous carbon fibers.
 15. The electrical device of claim 1, wherein the continuous fibers are electrically non-conductive before being infused with carbon nanotubes.
 16. The electrical device of claim 15, further comprising: a conductivity enhancer associated with the first electrode layer and the second electrode layer; wherein the conductivity enhancer comprises a metal form selected from the group consisting of metal foils, metal ribbons, metal powders, metal nanoparticles, and combinations thereof.
 17. The electrical device of claim 1, further comprising: an outer insulator casing.
 18. The electrical device of claim 17, wherein the outer insulator casing comprises a shrink wrap material.
 19. The electrical device of claim 1, wherein the electrical device comprises a supercapacitor.
 20. The electrical device of claim 19, wherein the supercapacitor has a capacitance of at least about 1 Farad/gram of continuous fibers.
 21. The electrical device of claim 20, wherein the supercapacitor has a capacitance of at least about 2 Farad/gram of continuous fibers.
 22. The electrical device of claim 1, wherein the infused carbon nanotubes are substantially perpendicular to the surface of the continuous fibers.
 23. The electrical device of claim 1, wherein the electrolyte comprises an inorganic electrolyte.
 24. The electrical device of claim 1, wherein the electrolyte comprises an organic electrolyte. 